Battery Thermal Wrap Silicone Rubber Sheets

  • 1
  • 2

Brand Name : FQ

Model Number : Rubber 1

Certification : IATF16949

Place of Origin : China

MOQ : Customized

Price : Fuzhou Fuqiang Precision Co.,Ltd.

Payment Terms : L/C, T/T, D/P

Supply Ability : 1000pcs/day

Delivery Time : 1000 pcs/ days

Packaging Details : pp bag+Cartons

Material : High flame retardant silicone rubber(buffer frame)

Contact Now

Main Features

Benefits of 70 Shore A Hardnes Silicone Rubber Sheets

  • 70 Shore A Hardness Blue Color Silicone Rubber Sheet has excellent fungus resistance and can be exposed to UV and ozone. Commercial grade silicone sheet with a smooth texture. Custom fabrication into seals and gaskets available upon request.

Battery Thermal Wrap Silicone Rubber Sheets

Specification

The main performance parameters are shown in Table

Serial number Test items Unit Test Standard SR No.
SR 35-A SR 40-A SR 50-A SR 60-A
1 Hardness Shore A GB/T531.1-2008 35±7 40±10 50±10 60±10
2 Density g/cm3 4.3.2 0.8≤μ±3σ≤1.4 1.00≤μ±3σ≤1.51 1.00≤μ±3σ≤1.51 1.1≤μ±3σ≤1.5
3 25 Compression curve MPa GB/T 7757-2009 10%:0.12≤μ±3σ≤0.22 10%:0.25≤μ±3σ≤0.53 10%:0.25≤μ±3σ≤0.75 10%: 0.45≤μ±3σ≤0.80
20%:0.25≤μ±3σ≤0.45 20%:0.50≤μ±3σ≤0.86 20%:0.63≤μ±3σ≤1.77 20%: 0.95≤μ±3σ≤1.45
30%:0.45≤μ±3σ≤0.7 30%:0.68≤μ±3σ≤1.32 30%:1.20≤μ±3σ≤2.24 30%: 1.50≤μ±3σ≤2.50
4 25 Shear performance under pressure Strength: µ-3σ≥0.8 Shear strength under pressure: µ-3σ≥0.5 Shear strength under pressure: µ-3σ≥0.2 Shear strength under pressure: µ-3σ≥0.8
Modulus: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75
5 25 Tensile strength MPa GB/T 528-2009 µ-3σ≥0.8 µ-3σ≥1.1 µ-3σ≥1.65 /
6 -30 Compression curve MPa GB/T 7757-2009 10%:0.08≤μ±3σ≤.0.22 10%:0.25≤μ±3σ≤0.53 10%:0.35≤μ±3σ≤0.65 10%:0.55≤μ±3σ≤0.90
20%:0.25≤μ±3σ≤0.45 20%:0.50≤μ±3σ≤0.86 20%:0.90≤μ±3σ≤1.20 20%:1.10≤μ±3σ≤1.95
30%:0.45≤μ±3σ≤0.9 30%:0.68≤μ±3σ≤1.32 30%:1.50≤μ±3σ≤2.00 30%: 2.00≤μ±3σ≤3.95
7 -30 Shear performance under pressure Strength: µ-3σ≥0.8 Shear strength under pressure: µ-3σ≥0.5 Shear strength under pressure: µ-3σ≥0.2 Shear strength under pressure: µ-3σ≥0.8
Modulus: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75
8 -30 Tensile strength MPa GB/T 528-2009 µ-3σ≥0.8 µ-3σ≥1.1 µ-3σ≥1.65 /
9 60 Compression curve MPa GB/T 7757-2009 10%:0.12≤μ±3σ≤0.22 10%:0.25≤μ±3σ≤0.53 10%:0.35≤μ±3σ≤0.70 10%: 0.35≤μ±3σ≤0.80
20%:0.25≤μ±3σ≤0.45 20%:0.50≤μ±3σ≤0.86 20%:0.80≤μ±3σ≤1.30 20%:0.65≤μ±3σ≤1.60
30%:0.45≤μ±3σ≤0.7 30%:0.68≤μ±3σ≤1.32 30%:1.00≤μ±3σ≤2.10 30%: 1.00≤μ±3σ≤2.50
10 60 Shear performance under pressure Strength: µ-3σ≥0.8 Shear strength under pressure: µ-3σ≥0.5 Shear strength under pressure: µ-3σ≥0.2 Shear strength under pressure: µ-3σ≥0.8
Modulus: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75
11 60 Tensile strength MPa GB/T 528-2009 µ-3σ≥0.8 µ-3σ≥1.1 µ-3σ≥1.65 /
12 Double 85 post-aging compression curve MPa GB/T 7757-2009 10%:0.12≤μ±3σ≤0.22 10%:0.25≤μ±3σ≤0.53 10%: 0.50≤μ±3σ≤0.70 10%: 0.40≤μ±3σ≤1.90
20%:0.25≤μ±3σ≤0.45 20%:0.50≤μ±3σ≤0.86 20%: 0.90≤μ±3σ≤1.30 20%: 1.00≤μ±3σ≤3.20
30%:0.45≤μ±3σ≤0.75 30%:0.68≤μ±3σ≤1.32 30%: 1.40≤μ±3σ≤2.10 30%: 1.70≤μ±3σ≤5.50
13 Double 85 post-aging shear performance under pressure Strength: µ-3σ≥0.8 Shear strength under pressure: µ-3σ≥0.5 Shear strength under pressure: µ-3σ≥0.2 Shear strength under pressure: µ-3σ≥0.8
Modulus: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75
14 Double 85 post-ageing Tensile strength MPa GB/T 528-2009 µ-3σ≥0.8 µ-3σ≥1.1 µ-3σ≥1.65 /
15 Compression curve after high and low-temperature cycle MPa GB/T 7757-2009 10%:0.12≤μ±3σ≤0.22 10%:0.25≤μ±3σ≤0.53 10%: 0.45≤μ±3σ≤0.65 10%: 0.50≤μ±3σ≤2.20
20%:0.25≤μ±3σ≤0.45 20%:0.50≤μ±3σ≤0.86 20%: 0.85≤μ±3σ≤1.35 20%: 1.00≤μ±3σ≤4.00
30%:0.45≤μ±3σ≤0.7 30%:0.68≤μ±3σ≤1.32 30%: 1.30≤μ±3σ≤2.50 30%: 1.80≤μ±3σ≤6.80
16 Shear performance under pressure after high and low temperature MPa ASTM C273C /273M-16 Strength: µ-3σ≥0.8 Shear strength under pressure: µ-3σ≥0.5 Shear strength under pressure: µ-3σ≥0.2 Shear strength under pressure: µ-3σ≥0.8
Modulus: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75 Shear modulus under pressure: Min≥0.75
17 Tensile strength after high and low-temperature cycle MPa GB/T 528-2009 µ-3σ≥0.8 µ-3σ≥1.1 µ-3σ≥1.65 /
18 Flame retardant / UL94 UL94 V0(2mm) V0(t≥2mm) V0(t≥2mm) V0(t≥2mm)
V1(1≤t2mm) V1(1≤t2mm) V1(1≤t2mm)
HB(0.4≤t1mm) HB(0.4≤t1mm) HB(0.4≤t1mm)
19 Forbidden object / RoHS &REACH & ELV RoHS &REACH & ELV RoHS &REACH & ELV RoHS &REACH & ELV RoHS &REACH & ELV
20 Insulation 1000V DC 60s µ-3σ≥500 µ-3σ≥500 µ-3σ≥500 µ-3σ≥500
21 Impedance mA 2700V DC 60s µ+3σ≤1 µ+3σ≤1 µ+3σ≤1 µ+3σ≤1
22 Thermal conductivity W/(m·K) GB/T 10295-2008 µ+3σ≤0.8 µ+3σ≤0.8 µ+3σ≤0.8 µ+3σ≤0.8
23 Specific heat capacity J/(g·K) ASTM E1269-2011 µ-3σ≥0.9 µ-3σ≥0.9 µ-3σ≥0.9 µ-3σ≥0.9
24 Stress retention rate % GB/T1685-2008 ≥40 ≥40 ≥40 ≥40
25 25 Shear strength with double-sided adhesive MPa ASTM D1002 Min≥0.8 Min≥0.8 Min≥1.1 Min≥1.5
26 -30 Shear strength with double-sided adhesive MPa ASTM D1002 Min≥0.6 Min≥0.8 Min≥1.1 Min≥1.5
27 60 Shear strength with double-sided adhesive MPa ASTM D1002 Min≥0.6 Min≥0.8 Min≥0.6 Min≥1.5
28 Double 85 ageing shear strength with double-sided adhesive MPa ASTM D1002 Min≥0.6 Min≥0.8 Min≥1.1 Min≥1.5
29 Shear strength after high and low-temperature cycles with double-sided adhesive MPa ASTM D1002 Min≥0.6 Min≥0.8 Min≥1.1 Min≥1.5

Industries

• Agriculture and Livestock
• Mining and Quarrying
• Mineral Processing
• Power Generation
• Construction
• Oil and Gas

Package & Delivery
Battery Thermal Wrap Silicone Rubber Sheets


Product Tags:

Thermal Wrap Silicone Rubber Sheets

      

Battery use Silicone Rubber Sheets

      
Best Battery Thermal Wrap Silicone Rubber Sheets wholesale

Battery Thermal Wrap Silicone Rubber Sheets Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Fuzhou Fuqiang Precision Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
Inquiry Cart 0